ZC-4111 35kV Inner Semiconductive Shield Compound

ZC-4111 Inner Semiconductive Shield Compound for MV Power Cable up to 35kV

Description

This material is used for crosslinkable semiconductive wire and cable shielding material. It is made of high quality EVA resin, conductive black carbon as the main material, adding cross-linking agent, antioxidant and other additives; mixed granulation and fabrication process is stable and reliable in quality.

Application

- Shielding material of 35kV crosslinkable polyethylene insulated cable conductor;

- Maximum working temperature is 90℃.

Property

Item		Unit	Test method	Typical value
Density@23℃		g/cm³	ASTM D792	1.12
Tensile strength		MPa	IEC60811-1-1	17.0
Elongation at break		%	IEC60811-1-1	308
Impact embrittlement performance@-40℃	Failure number	Piece	ASTM D746	0/30
After aging @135℃, 168h	Tensile strength variation	%	IEC 60811-1-2	+7
After aging @135℃, 168h	Breaking elongation variation	%	IEC 60811-1-2	-5
Hot prolongation@200℃, 0.2MPa, 15min	Elongation under the load	%	IEC 60811-2-1	50
Hot prolongation@200℃, 0.2MPa, 15min	Permanent deformation	%	IEC 60811-2-1	0
Volume resistivity@20℃		Ω·cm	ASTM D257	25
Volume resistivity@90℃		Ω·cm	ASTM D257	240

Processing

Recommend for polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance. Recommend to use 60 to 80 type wire mesh filter.

Zone	1	2	3	4	5	Neck	Head	Die
Temperature Range℃	75	85	105	115	115	115	115	115

- Above temperature is only for reference.

Storage

- Keep at room temperature;

- Storage environment should be clean, dry and ventilated;

- Please dry it after a long-time opening.

Product packing

- 600kg in each package;

- Inner lined with plastic sealed film bag;

- Corrugated carton with tray at the bottom.